<div><div><div>Dear colleagues,</div><div> </div><div>we have tried to perfom band structure DFT-calculation of crystall SrTiO3 with hybrid functionals.</div><div>When we run tests with silicon from the QE package it was OK.</div><div> </div><div>But when we tried SrTiO3 following to the "fake" procedure in Si example, we've got sharp peaks in band structure graph.</div><div>We have used PBE0 and HSE functionals with US pseudopotentials. The result was the same.</div><div>Furthermore, despite we used  nqx1 = 2  nqx2 = 2  nqx3 = 2 in scf-input, </div><div>in scf-output there is the record:  EXX: q-point mesh:     1    1    1</div><div> </div><div>Input-file:</div><div> </div><div>&CONTROL</div><div>  calculation = "scf"</div><div>  restart_mode='from_scratch',</div><div>  prefix = 'SrTiO3',</div><div>  nstep       = 900,</div><div>  max_seconds =  8.64000e+04</div><div>  pseudo_dir  = "/home/QuantumEspresso/pseudo",</div><div>  wf_collect = .true.</div><div>  etot_conv_thr   =  1.0d-8</div><div>  verbosity ='high'</div><div>/</div><div> </div><div>&SYSTEM</div><div>    ibrav  = 1,</div><div>    a =  3.8931e+00,</div><div>    nat=5,</div><div>    ntyp=3,</div><div>    occupations='smearing',</div><div>    smearing   ='gauss',  </div><div>    degauss    = 0.005,  </div><div>    nspin= 1</div><div>    ecutwfc = 55.0d0</div><div>    ecutrho = 580.d0  </div><div>    input_dft = 'hse',</div><div>    nqx1 = 2          </div><div>    nqx2 = 2</div><div>    nqx3 = 2</div><div>/</div><div> </div><div>&ELECTRONS</div><div>    electron_maxstep = 800</div><div>    conv_thr         =  1.0d-8</div><div>    mixing_beta      =  0.3</div><div>/</div><div>&IONS</div><div>ion_dynamics ='bfgs'</div><div>/</div><div>&CELL</div><div> </div><div>/</div><div>ATOMIC_SPECIES</div><div>O     15.9994  O.pbesol-n-rrkjus_psl.1.0.0.UPF</div><div>Sr    87.6200  Sr.pbesol-spn-rrkjus_psl.1.0.0.UPF</div><div>Ti    47.8670  Ti.pbesol-spn-rrkjus_psl.1.0.0.UPF</div><div> </div><div>ATOMIC_POSITIONS {crystal}</div><div>   O           0.5           0.0           0.5</div><div>   O           0.5           0.5           0.0</div><div>   O           0.0           0.5           0.5</div><div>   Sr          0.0           0.0           0.0</div><div>   Ti           0.5           0.5           0.5</div><div> </div><div>K_POINTS automatic  </div><div> 8 8 8 0 0 0 </div><div>ADDITIONAL_K_POINTS tpiba_b   </div><div> 8  </div><div>   0.0000000000     0.0000000000     0.0000000000   20   ! GAMMA</div><div>   0.0000000000     0.5000000000     0.0000000000   20   ! X</div><div>   0.5000000000     0.5000000000     0.0000000000   28   ! M</div><div>   0.0000000000     0.0000000000     0.0000000000   36   ! GAMMA</div><div>   0.5000000000     0.5000000000     0.5000000000   28   ! R</div><div>   0.0000000000     0.5000000000     0.0000000000    0   ! X</div><div>   0.5000000000     0.5000000000     0.0000000000   20   ! M</div><div>   0.5000000000     0.5000000000     0.5000000000    0   ! R</div><div> </div><div>Would you answer my question, is there a way to get appropriate band structure picture with hybrid functional using the "fake" procedure?</div><div> </div><div>Regards, </div><div>Gavrikov Anton, </div><div>PhD, researcher,</div><div>Saint-Petersburg State University.</div></div></div><div> </div>